2K polyester putty with aluminum powder

Carcoat Metallic is a filling compound that contains aluminum powder, which enhances its ability to withstand high temperatures and ensures strong adhesion to various surfaces. Its lower shrinkage compared to ordinary putties and high elasticity make it suitable for repairing large defects.

The surface should be sanded and then degreased with a cleaning solvent.

Mix homogeneously with sufficient hardener (2-3%). Pot life: 3-5 mins.

Apply the putty with putty spatulas, flexible rubber or plastic spreaders.

Drying time: 20-30 mins, at a temperature close to 20°C.

Sand with P80 - P120 grit until the desired surface is obtained and finish with P120 - P240

Wear respiratory protection during application

Frequently Asked Questions About This Putty


• Resistance to high temperature
• Excellent adhesion to surfaces
• Low shrinkage
• High filling power and flexibility
• Easy to sand
• Highly concentrated filler
• Very easy and pore-free to work

The Available Packaging

• 1 Kg • 2 Kg • 500 gr


For professional use only. Do not return unused mixed material into the can. Make applications where ventilation is sufficient. Keep away from heat, sparks, flame, hot surfaces. Vapors may cause flash fire. Causes eyes and skin irritation. Do not breathe vapors. Use required personal protective equipment. In case of contact with eyes or skin, rinse immediately with plenty of water. For more information see the SDS.

Physical Characteristics

• Color: Silver
• Basis: polyester resin with a pigment-filler-combination
• Drying time (at 20°C, 50% relative air humidity): 20-30 min
• Pot life / Working time at 20°C: 3-5 min
• Color of hardener: Red
• Delivery viscosity at 20°C: as a paste
• VOC content: 2004/42/IIB (b) (250) < 250g/l
• Minimum application temperature: +5°C


It should be kept in a tightly covered container, in a dry and ventilated place, avoiding direct exposure to sunlight. Temperature above 5°C is recommended, Temperature between 15 and 30°C is optimal. Improper storage conditions shorten the shelf life of the product.

Volatile Organic Compounds

The VOC content of this putty is a maximum of 250 g/l in compliance with European standard 2004/42/CE IIB(B) (250) <250 g/l.

Hardener Percentage Temperature
Benzoyl Peroxide Paste 50% 3% 5-10°C
Benzoyl Peroxide Paste 50% 2% 10-20°C
Benzoyl Peroxide Paste 50% 1% >20°C